SS316L PLATE
2023-11-21
The Mo content of 316L makes this steel type have excellent corrosion resistance and can be safely used in environments containing halogen ions such as Cl-. Since 316L is mainly used for its chemical properties, steel mills have slightly lower surface inspection requirements for 316L (compared to 304). Customers with higher surface requirements should strengthen surface inspection.
chemical composition
Carbon C: ≤0.030
Silicon Si: ≤1.00
Manganese Mn: ≤2.00
Sulfur S: ≤0.030
Phosphorus P: ≤0.045
Chromium Cr: 16.00~18.00
Nickel Ni: 10.00~14.00
Molybdenum Mo: 2.00~3.00
Mechanical properties
Tensile strength σb (MPa): ≥480
Conditional yield strength σ0.2 (MPa): ≥177
Elongation δ5 (%): ≥40
Reduction of area ψ (%): ≥60
Hardness: ≤187HB; ≤90HRB; ≤200HV
Density: 7.98g/cm3;
Specific heat capacity ratio (20℃): 0.502J/(g*K)